Product: MIP-202(Zr)
Synonyms: NA
CAS：2378179-91-8
Basic Information
| Unit MF. | C24H30O32N6Zr6 | Unit MW. | 1461.86 | ||
| Coordination Metal | Zr | Linkers | L-aspartic acid (CAS：617-45-8) | ||
| Pore Size | <0.7nm | Pore volume | 0.139 (Vm)/0.508 (Vt) cm3/g | ||
| Surface Area | no N2 sorption, | ||||
| Analog Structure |   |
||||
Product Property
| Appearance | White Powder |  |
||
| Particle Size | 200nm nanoparticles | |||
Stability
1) MIP-202(Zr) is stable in air, stable in bioling water and acidic conditions(stable in PH 0-11)
2）High thermal stability, thermal decomposition temperature about 200 ° C
2）High thermal stability, thermal decomposition temperature about 200 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to activate for 12 hours at 80 degree in vacuum.
2) It is recommended to activate for 12 hours at 80 degree in vacuum.
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption. Good proton conductivity.
2) MIP-202 is easily prepared at 100-gram scale.
2) MIP-202 is easily prepared at 100-gram scale.
3) MIP-202 could be calcinated to N-doped porous carbons.
Characterizations
References
1) Wang, S., Wahiduzzaman, M., Davis, L. et al. Nat Commun 2018, 9, 4937 DOI: 10.1038/s41467-018-07414-4 ; A robust zirconium amino acid metal-organic framework for proton conduction