Product: Co-Zn-ZIF
Synonyms: ZIF-Zn/Co, ZIF-8/ZIF-67 Mixed MOF
CAS：/
Basic Information
| Unit MF. | C8H10N4Zn | Unit MW. | 227.5818 | ||
| Coordination Metal | Zn/Co (1:1 Reactant) | Linkers | 2-Methylimidazole（CAS：693-98-1） | ||
| Aperture | 0.34nm; 1.1nm | Pore volume | 0.66 cm3/g | ||
| Surface Area | BET Specific surface 1200 m2/g, | ||||
| Analog Structure |    |
||||
Product Property
| Appearance | Purple Powder |  |
||
| Particle Size | 300-600nm | |||
Stability
1) ZIF-Co/Zn is stable in air, stable in aqueous and strong alkaline conditions, instable in acidic condition
2) High thermal stability, thermal decomposition temperature above 400 ° C
2) High thermal stability, thermal decomposition temperature above 400 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to activate for 12 hours at 120 degree in vacuum before gas adsorption test
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) Good drug carrier, which is able to decompose in stomach and release the drug content
2) Good drug carrier, which is able to decompose in stomach and release the drug content
Characterizations
References
1) Huang, Xiao-Chun; Lin, Yan-Yong; Zhang, Jie-Peng; Chen, Xiao-Ming; Angew. Chem. Int. Ed. 2006, 45, 1557-1559, DOI: 10.1002/anie.200503778 ; Ligand-directed strategy for zeolite-type metal-organic frameworks: zinc(II) imidazolates with unusual zeolitic topologies
2) Park, Kyo Sung; Ni, Zheng; Cote, Adrien P.; Choi, Jae Yong; Huang, Rudan; Uribe-Romo, Fernando J.; Chae, Hee K.; O'Keeffe, Michael; Yaghi, Omar M.; Proc. Natl. Acad. Sci. USA 2006, 103, 10186-10191, DOI: 10.1073/pnas.0602439103 ; Exceptional chemical and thermal stability of zeolitic imidazolate frameworks
3) Liu, Chang; Tong, Yu-Long; Yu, Xiao-Qing; Shen, Haixia; Zhu, Zhijie; Li, Qing; Chen, Su; ACS Appl. Mater. Interfaces 2020, 12, 2, 2816–2825, DOI: 10.1021/acsami.9b18012 ; MOF-Based Photonic Crystal Film toward Separation of Organic Dyes