Product: UIO-66-OH
Synonyms: OH-UIO-66
CAS：1334721-91-3
Basic Information
| Unit MF. | C48H24O38Zr6 | Unit MW. | 1756.02 | ||
| Coordination Metal | Zr | Linkers | 2-hydroxyterephthalic acid (CAS：636-94-2) | ||
| Pore Size | 0.7nm; 1.0nm | Pore volume | 0.4 cm3/g | ||
| Surface Area | BET Specific surface 700 m2/g, | ||||
| Analog Structure |   |
||||
Product Property
| Appearance | Off-White/Light Yellow Powder |  |
||
| Particle Size | 100-300nm | |||
Stability
1) UIO-66-OH is stable in air, stable in aqueous and acidic conditions(stable in PH 1-12)
2）High thermal stability, thermal decomposition temperature above 350 ° C
2）High thermal stability, thermal decomposition temperature above 350 ° C
Preservation
1) Keep sealed in dry and cool condition
2) It is recommended to activate for 12 hours at 120 degree in vacuum.
2) It is recommended to activate for 12 hours at 120 degree in vacuum.
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) UIO-66-OH, with brach hydroxyl groups, could be further derivated in biochemical research
2) UIO-66-OH, with brach hydroxyl groups, could be further derivated in biochemical research
Characterizations
References
1) Yang, Qingyuan; Wiersum, Andrew D.; Llewellyn, Philip L.; Guillerm, Vincent; Serre, Christian; Maurin, Guillaume; Chem. Commun. 2011, 47(34), 9603-9605, Functionalizing porous zirconium terephthalate UiO-66(Zr) for natural gas upgrading based on a computational exploration
2) Katz, Michael J.; Brown, Zachary J.; Colon, Yamil J.; Siu, Paul W.; Scheidt, Karl A.; Snurr, Randall Q.; Hupp, Joseph T.; Farha, Omar K.; Chem. Commun. 2013, 49(82), 9449-9451, DOI: 10.1039/c3cc46105j ; A facile synthesis of UiO-66, UiO-67 and their derivatives