Product：TSCOF-1
Synonyms：2D-NTCDA-TTTA COF ; NTCDA-TAPT COF
CAS：1426152-92-2
Synonyms：2D-NTCDA-TTTA COF ; NTCDA-TAPT COF
CAS：1426152-92-2
Basic Information
| Unit MF. | (C21H18N6.C14H4O6)x | Unit MW. | |||
| Linkers |
1) 1,4,5,8-naphthalene tetracarboxylic anhydride (CAS: 81-30-1 ); 2) 1,4-benzenediamine (CAS:106-50-3) |
||||
| Pore Size | 4nm (1-1.3nm) | Pore volume | 0.3cm3/g | ||
| Surface Area | BET Specific surface 700-1000 m2/g | ||||
| Analog Structure | |||||
Product Property
| Appearance |
Brown Solid |
 |
||
| Particle Size | irregular clusters | |||
Stability
1) Stable in aqueous solution, stable in acidic and alkaline conditions
2) Good thermal stablility, thermal decomposition temperature above 400℃
Preservation
1) Dry and sealed under normal temperature or low temperature conditions
Other Features
Fluorescence: NA
Applications
1) For gas and pollutant adsorption
2) Rigid pores to load other catalysts
2) Rigid pores to load other catalysts
Characterizations
References
1) Liebl, Mario R.; Senker, Juergen; Chemistry of Materials 2013, 25(6), 970-980, DOI: 10.1021/cm4000894 ; Microporous Functionalized Triazine-Based Polyimides with High CO2 Capture Capacity
2) Patent：CN110218317A Preparation method of polyimide covalent organic framework for energy storage device electrode
3) Patent：CN114773556A Green solid phase synthesis method covalent organic framework material
4) Liu, Yannan ; Lu, Yiyue; Hossain Khan, Arafat; Wang, Gang ; Wang, Yong; Morag, Ahiud; Wang, Zhiyong; Chen, Guangbo; Huang, Shengyun; Chandrasekhar, Naisa; Sabaghi, Davood; Li, Dongqi; Zhang, Panpan; Ma, Dongling ; Brunner, Eike; Yu, Minghao; Feng, Xinliang; Angew. Chem., Int. Ed. 2023, 62(30), e202306091, DOI: 10.1002/anie.202306091; Redox-Bipolar Polyimide Two-Dimensional Covalent Organic Framework Cathodes for Durable Aluminium Batteries
| XRD TSCOF-1-CS018206.pdf | Download |