Home > Product Category > MOF Materials > MOFs by Applications > Nanosized MOF Particles
CAS NO.:Formula:C48H28O32Zr6Weight: 1664.06

Product: UIO-66 nanoparticles
Synonyms: NA
CAS:1072413-89-8

Basic Information
Unit MF. C48H24O32Zr6 Unit MW. 1660.03
Coordination  Metal Zr Linkers Terephthalic acid (CAS: 100-21-0)
Pore Size 0.8nm; 1.1nm Pore volume 0.5 cm3/g
Surface Area BET Specific surface >1000 m2/g,
Analog Structure   
Product Property
Appearance White Powder  
Particle Size 200nm-1um
Stability
1) UIO-66 is stable in air, stable in aqueous and acidic conditions(stable in PH 1-12)
2)High thermal stability, thermal decomposition temperature above 400 ° C
Preservation
1) Keep sealed in dry and cool condition 
2) It is recommended to degas for 12 hours at 120 degree in vacuum before gas-adsorption test.
3) Ultrasonic despersion in methanol/ethanol/DMF before in-vitro test
Other Features
Fluorescence:NA
Applications
1) Gas (such as carbon dioxide) and pollutant adsorption
2) UIO-66 has very rigid framework, which is good carrier of catalyst.
Characterizations
XRD
SEM
SEM-UIO-66 nanoparticles s
BET
BET-UIO-66 nanoparticles
FTIR
NA
References
1) J. H. Cavka, S. Jakobsen, U. Olsbye, N. Guillou, C. Lamberti, S. Bordiga, K. P. Lillerud, J. Am. Chem. Soc. 2008, 130, 13850-13851, DOI: 10.1021/ja8057953 ; A New Zirconium Inorganic Building Brick Forming Metal Organic Frameworks with Exceptional Stability
2) S. J. Garibaya, S. M. Cohen, Chem. Commun., 2010,46, 7700-7702, DOI: 10.1039/C0CC02990D ; Isoreticular synthesis and modification of frameworks with the UiO-66 topology
3) P.Yang, F. Mao, Y. Li, Q. Zhuang, J. Gu, Chem. Eur. J. 2018, 24, 2962-2970, DOI : 10.1002/chem.201705020 ; Hierarchical Porous Zr‐Based MOFs Synthesized by a Facile Monocarboxylic Acid Etching Strategy